Vestnik of Samara State Technical University. Technical Sciences SeriesVestnik of Samara State Technical University. Technical Sciences Series1991-85422712-8938Samara State Technical University2024110.14498/tech.2016.4.%uResearch ArticleAnalysis of the possible causes of failure of good smooth drill pipeSuslinaAnastasiya AGraduate Student-KoshcheevKirill IBachelor-PugachevaTatiana MTatiana M. Pugacheva-Samara State Technical University1512201624415816210022020Copyright © 2016, Samara State Technical University2016The analysis of reasons for emergency destruction of light alloy drill pipes is given. During the examination the studied macro - and microstructure of damaged structural areas of the metal drill pipe and the chemical composition of the metal, characteristics of strength, ductility and hardness are defined. The conclusions on drill pipe quality were made. The main reasons of quick drill pipe wear during operation were named.aluminum drilling pipechemical compositionmechanical propertiesmicrostructuremetallurgical qualitycauses of wearлегкосплавная бурильная трубахимический составмеханические свойствамикроструктураметаллургическое качествопричины износа[Абубакиров В.Ф. Оборудование буровое, противовыбросовое и устьевое: В 2 т. Т. 2. - М.: ИРЦ, Газпром, 2007. - 650 с.][Калинин А.Г., Григорян Н.А., Султанов Б.З. Бурение наклонных скважин: справочник. - М.: Недра, 1990. - 348 с.][Ежов И.В. Бурение наклонных и горизонтальных скважин: Учеб. пособие. - М.: Феникс, 2016. - 288 с.][Штамбург В.Ф., Фаин Г.М., Данелянц С.М., Шеина А.А. Бурильные трубы из алюминиевых сплавов. - М.: Недра, 1980. - 240 с.][Коррозионно-усталостная прочность бурильных труб из алюминиевых сплавов / А.В. Карлашов, А.Н. Яров, К.М. Гильман и др. - М.: Недра, 1977. - 183 с.]