Influence of hydrothermal synthesis conditions on microstructure characteristics of copper nanowires

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅或者付费存取

详细

The dependence of the microstructural properties of copper nanowires on temperature (110, 120 and 130°C) and time (4 and 8 h) has been studied for the hydrothermal synthesis of copper nanowires using oleylamine and dextrose. The change in diameter of the Cu nanowires formed was monitored by spectrophotometry in the visible range. X-ray diffraction analysis was used to confirm the target crystal structure and the absence of copper oxide impurities, as well as to show the nonlinear dependence of the average size of the coherent scattering region on the temperature and duration of the synthesis process. The scanning electron microscopy results showed that, in general, increasing the temperature and duration of the synthesis process leads to an increase in the length of the formed copper nanowires from 45 to 150 μm, i.e. under certain conditions, ultra-long structures are obtained. As a result, the aspect ratio varies from 782 to 2358 by altering the synthesis conditions. Transmission electron microscopy shows that the sample obtained at 110°C (4 h) differs from the others by the presence of particles up to 10 nm in size on the surface of the nanowires. The microstructural parameters of the obtained materials were also studied by atomic force microscopy, and the values of the electronic work function of the individual copper nanowire surface in ambient atmosphere were determined by Kelvin probe force microscopy.

全文:

受限制的访问

作者简介

N. Simonenko

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

编辑信件的主要联系方式.
Email: n_simonenko@mail.ru
俄罗斯联邦, Moscow, 119991

T. Simonenko

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: n_simonenko@mail.ru
俄罗斯联邦, Moscow, 119991

Ya. Topalova

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: n_simonenko@mail.ru
俄罗斯联邦, Moscow, 119991

Ph. Gorobtsov

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: n_simonenko@mail.ru
俄罗斯联邦, Moscow, 119991

P. Arsenov

Moscow Institute of Physics and Technology (National Research University)

Email: n_simonenko@mail.ru
俄罗斯联邦, Dolgoprudny, Moscow Region, 141701

E. Simonenko

Kurnakov Institute of General and Inorganic Chemistry of the Russian Academy of Sciences

Email: n_simonenko@mail.ru
俄罗斯联邦, Moscow, 119991

参考

  1. Huang S., Liu Y., Yang F. et al. // Environ. Chem. Lett. 2022. V. 20. № 5. P. 3005. https://doi.org/10.1007/s10311-022-01471-4
  2. Ding Y., Xiong S., Sun L. et al. // Chem. Soc. Rev. 2024. V. 53. № 15. P. 7784. https://doi.org/10.1039/D4CS00080C
  3. Simonenko N.P., Simonenko T.L., Gorobtsov P.Y. et al. // Russ. J. Inorg. Chem. 2024. V. 69. P. 1265. https://doi.org/10.1134/S0036023624601685
  4. Hwang H., Kim A., Zhong Z. et al. // Adv. Funct. Mater. 2016. V. 26. № 36. P. 6545. https://doi.org/10.1002/adfm.201602094
  5. Arsenov P.V., Pilyushenko K.S., Mikhailova P.S. et al. // Nano-Structures Nano-Objects. 2025. V. 41. P. 101429. https://doi.org/10.1016/j.nanoso.2024.101429
  6. Simonenko N.P., Simonenko T.L., Gorobtsov P.Y. et al. // Russ. J. Inorg. Chem. 2024. V. 69. P. 1301. https://doi.org/10.1134/S0036023624601697
  7. Nam V., Lee D. // Nanomaterials. 2016. V. 6. № 3. P. 47. https://doi.org/10.3390/nano6030047
  8. Wang Y., Liu P., Zeng B. et al. // Nanoscale Res. Lett. 2018. V. 13. № 1. P. 78. https://doi.org/10.1186/s11671-018-2486-5
  9. Zhao S., Han F., Li J. et al. // Small. 2018. V. 14. № 26. https://doi.org/10.1002/smll.201800047
  10. Hwang C., An J., Choi B.D. et al. // J. Mater. Chem. C. 2016. V. 4. № 7. P. 1441. https://doi.org/10.1039/C5TC03614C
  11. Chiu J.-M., Wahdini I., Shen Y.-N. et al. // ACS Appl. Energy Mater. 2023. V. 6. № 9. P. 5058. https://doi.org/10.1021/acsaem.3c00703
  12. Li X., Wang Y., Yin C. et al. // J. Mater. Chem. C. 2020. V. 8. № 3. P. 849. https://doi.org/10.1039/C9TC04744A
  13. Yoon H., Shin D.S., Kim T.G. et al. // ACS Sustain. Chem. Eng. 2018. V. 6. № 11. P. 13888. https://doi.org/10.1021/acssuschemeng.8b02135
  14. Zhao Y., Zhang Y., Li Y. et al. // New J. Chem. 2012. V. 36. № 5. P. 1161. https://doi.org/10.1039/c2nj21026f
  15. Yu L., Wang Y., Wang J. et al. // Sens. Actuators, A: Phys. 2022. V. 334. P. 113362. https://doi.org/10.1016/j.sna.2021.113362
  16. Lah N.A.C., Trigueros S. // Sci. Technol. Adv. Mater. 2019. V. 20. № 1. P. 225. https://doi.org/10.1080/14686996.2019.1585145
  17. Kalinin I.A., Davydov A.D., Leontiev A.P. et al. // Electrochim. Acta. 2023. V. 441. P. 141766. https://doi.org/10.1016/j.electacta.2022.141766
  18. Bograchev D.A., Kabanova T.B., Davydov A.D. // J. Solid State Electrochem. 2025. V. 29. № 4. P. 1309. https://doi.org/10.1007/s10008-024-06118-8
  19. Khalil A., Hashaikeh R., Jouiad M. // J. Mater. Sci. 2014. V. 49. № 8. P. 3052. https://doi.org/10.1007/s10853-013-8005-2
  20. Kim N.K., Kim K., Jang H. et al. // Sci. Rep. 2023. V. 13. № 1. P. 22248. https://doi.org/10.1038/s41598-023-49741-7
  21. Cuya Huaman J.L., Urushizaki I., Jeyadevan B. // J. Nanomater. 2018. V. 2018. P. 1. https://doi.org/10.1155/2018/1698357
  22. Hosseini M., Fatmehsari D.H., Marashi S.P.H. // Appl. Phys. A. 2015. V. 120. № 4. P. 1579. https://doi.org/10.1007/s00339-015-9358-y
  23. Koo J., Lee C., Chu C.R. et al. // Adv. Mater. Technol. 2020. V. 5. № 4. https://doi.org/10.1002/admt.201900962
  24. Zha X., Gong D., Chen W. et al. // Nanomaterials. 2025. V. 15. № 9. P. 638. https://doi.org/10.3390/nano15090638
  25. Hong W., Wang J., Wang E. // Nanoscale. 2016. V. 8. № 9. P. 4927. https://doi.org/10.1039/C5NR07516E
  26. Ohiienko O., Oh Y.-J. // Mater. Chem. Phys. 2020. V. 246. P. 122783. https://doi.org/10.1016/j.matchemphys.2020.122783
  27. Conte A., Rosati A., Fantin M. et al. // Mater. Adv. 2024. V. 5. № 22. P. 8836. https://doi.org/10.1039/D4MA00402G
  28. Kim J., Kim M., Jung H. et al. // Nano Energy. 2023. V. 106. P. 108067. https://doi.org/10.1016/j.nanoen.2022.108067
  29. Ravi Kumar D. V., Woo K., Moon J. // Nanoscale. 2015. V. 7. № 41. P. 17195. https://doi.org/10.1039/C5NR05138J
  30. Duong T.-H., Kim H.-C. // Int. Nano Lett. 2017. V. 7. № 2. P. 165. https://doi.org/10.1007/s40089-017-0204-4
  31. Hadaoui S., Tran G., Naitabdi A. et al. // Nanoscale. 2025. V. 17. № 6. P. 3277. https://doi.org/10.1039/D4NR04079A
  32. Li Y., Fan Z., Yuan X. et al. // Mater. Lett. 2020. V. 274. P. 128029. https://doi.org/10.1016/j.matlet.2020.128029
  33. Ding S., Tian Y. // RSC Adv. 2019. V. 9. № 46. P. 26961. https://doi.org/10.1039/C9RA04404C
  34. Ravi Kumar D.V., Kim I., Zhong Z. et al. // Phys. Chem. Chem. Phys. 2014. V. 16. № 40. P. 22107. https://doi.org/10.1039/C4CP03880K
  35. Lu P.-W., Jaihao C., Pan L.-C. et al. // Polymers (Basel). 2022. V. 14. № 16. P. 3369. https://doi.org/10.3390/polym14163369
  36. Duong T.-H., Kim H.-C. // Ind. Eng. Chem. Res. 2018. V. 57. № 8. P. 3076. https://doi.org/10.1021/acs.iecr.7b04709
  37. Lewis C.S., Wang L., Liu H. et al. // Cryst. Growth Des. 2014. V. 14. № 8. P. 3825. https://doi.org/10.1021/cg500324j
  38. Liu G., Wang J., Ge Y. et al. // ACS Nano. 2020. V. 14. № 6. P. 6761. https://doi.org/10.1021/acsnano.0c00109
  39. Shahzad Khan B., Mehmood T., Mukhtar A. et al. // Mater. Lett. 2014. V. 137. P. 13. https://doi.org/10.1016/j.matlet.2014.08.095

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. Visible and near infrared absorption spectra for samples 2, 4, and 6, which are dispersed systems based on copper nanowires and isopropyl alcohol.

下载 (14KB)
索引源数据
3. Fig. 2. X-ray diffraction patterns of films based on synthesized copper nanowires (samples 1–6).

下载 (18KB)
索引源数据
4. Fig. 3. Average CSR size (black markers; according to X-ray diffraction data) and average diameter (red markers; according to SEM data) for Cu nanowires obtained under different synthesis conditions.

下载 (125KB)
索引源数据
5. Fig. 4. Microstructure of copper nanowires obtained under different conditions (according to SEM data).

下载 (16KB)
索引源数据
6. Fig. 5. Microstructure of the obtained copper nanowires (a — sample 1, b — 2, c — 3, d — 4, e — 5, e — 6; according to TEM data).

下载 (53KB)
索引源数据
7. Fig. 6. Microstructure of the obtained copper nanowires (a — sample 1, b — 2, c — 3, d — 4, d — 5, e — 6; according to AFM data).

下载 (108KB)
索引源数据
8. Fig. 7. Values of the diameter of Cu nanowires obtained under different conditions (according to AFM data).

下载 (12KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2025