Experimental results of the application of eristic synthesis to create a promising instrument

Cover Page

Cite item

Full Text

Open Access Open Access
Restricted Access Access granted
Restricted Access Subscription or Fee Access

Abstract

The application of the heuristic synthesis algorithm is considered on the example of the problem of adhesive setting during reduction. The steps of its application in comprehensive reduction are consistently shown and described. The results obtained during experimental studies are presented, technical recommendations are given, implemented on the example of manufacturing a shaped
mandrel.

Full Text

Restricted Access

About the authors

V. А. Kuznetsov

ФГБОУ ВО «МГТУ «СТАНКИН»

Author for correspondence.
Email: journal@electronics.ru

доктор технических наук, профессор, заведующий кафедрой «Инструментальная техника и технологии формообразования»

Russian Federation, Москва

A. A. Kostryukov

АО «Демиховский машиностроительный завод»

Email: journal@electronics.ru

руководитель направления отдела главного технолога, АО «Демиховский машиностроительный завод»

Russian Federation, Московская обл., Орехово-Зуевский г. о.

References

  1. Щедрин А. В., Кострюков А. А. Применение триботехнологий на основе самоорганизации для системного совершенствования процессов холодного пластического деформирования // Упрочняющие технологии и покрытия. 2017. Т. 13. № 11. С. 495–499.
  2. Щедрин А. В., Алёшин В.Ф., Бугаев А.М. и др. Теоретико-экспериментальные исследование и совершенствование методов дорнования отверстий инструментом с регулярной микрогеометрией поверхности в условиях применения металлоплакирующих смазок // Упрочняющие технология и покрытия. 2019. Т. 15. № 11. С. 501–505.
  3. Щедрин А. В., Кострюков А. А., Чихачёва Н. Ю. и др. Технологические возможности метода комбинированного прошивания отверстий с противодавлением металлоплакирующих смазок // Сборка в машиностроении, приборостроении. 2016. № 9. С. 30–35.
  4. Кузнецов В. А., Черепахин А. А., Смирнов А. В. Системный анализ и моделирование технологических методов изготовления детали. М.: Компания КноРус, 2019.
  5. Кузнецов В. А., Кострюков А. А. Эвристический синтез как инструмент создания перспективного инструмента// Упрочняющие технологии и покрытия. 2024. Т. 20. № 4. С. 147–149.
  6. Kostryukov A. A., Shchedrin A. V., Bekaev A. A. Predicting the drawing force for cylindrical blanks with modified surface layer // Russian engineering research. 2020. Vol. 40. No. 5. PP. 407–412.
  7. Fanidi O., Kostryukov A., Shchedrin A. Predicting the burnishing force for cylindrical workpieces with amodified surface layer // Strojnicky casopis. 2022. Vol. 72. No. 1. PP. 35–48.

Supplementary files

Supplementary Files
Action
1. JATS XML
Download
2. Fig. 1. Algorithm of heuristic synthesis of the processing method relative to the selected prototype

Download (214KB)
Indexing metadata
3. Fig. 2. Tuning fork type device

Download (334KB)
Indexing metadata
4. Fig. 3. Regular microrelief on the surface of the workpieces

Download (583KB)
Indexing metadata
5. Fig. 4. Regular microrelief on the surface of the working channel of the die

Download (194KB)
Indexing metadata
6. Fig. 5. Dependence of the specific reduction force on the interference fit, nature and parameters of the microgeometry of the acting tool surface and the surface of the workpieces (steel 20, 156 HB): 1 - tool and workpieces with IMR surface (I-40 lubricant); 2 - tool with RMR, workpieces with IMR surface (Gk = 0 μm, I-40 lubricant + 50% MPS "Valena"); 3 - tool with RMR, workpieces with RMR surface (Gk = 18 μm, I-40 lubricant + 50% MPS "Valena"); 4 - tool with RMR, workpieces with RMR surface (Gk = 25 μm, I-40 lubricant + 50% MPS "Valena"); 5 – tool with RMR, workpieces with RMR surface (Gk = 30 µm, lubricant I-40 + 50% MPS “Valena”)

Download (71KB)
Indexing metadata
7. Fig. 6. Dependence of the specific reduction force on the tension (designations 1–5 see Fig. 5)

Download (63KB)
Indexing metadata
8. Fig. 7. Characteristic profiles of parts obtained by reducing blanks with a surface RMR (Гк = 25 μm) with a tool with RMR (lubricant I-40 + 50% MPS "Valena"): a - iф = 0.122 mm; b - iф = 0.23 mm; c - iф = 0.323 mm; g - iф = 0.3916 mm; d - iф = 0.5133 mm.

Download (206KB)
Indexing metadata
9. Fig. 8. Characteristic profiles of parts obtained by reducing blanks with a surface RMR (Гк = 30 μm) with a tool with RMR (lubricant I-40 + 50% MPS "Valena"): a - iф = 0.185 mm; b - iф = 0.558 mm

Download (101KB)
Indexing metadata
10. Fig. 9. Dependence of the scattering field of the diameter of parts on the interference fit (steel 20, 156 HB) (designations 1–5 see Fig. 5)

Download (50KB)
Indexing metadata
11. Fig. 10. Dependence of the average deviation of the longitudinal section (LS) profile of parts on the interference fit (steel 20, 156 HB) (designations 1–5 see Fig. 5)

Download (58KB)
Indexing metadata
12. Fig. 11. Dependence of the average ovality of parts (OD) on the interference (steel 20) (designations 1–5 see Fig. 5)

Download (56KB)
Indexing metadata
13. Fig. 12. Sketch of a fragment of a shaped mandrel

Download (52KB)
Indexing metadata
14. Fig. 13. Sketch of the tool for applying RMR: 1 – cassette with granules, 2 – body, 3 – cover, 4 – screws

Download (112KB)
Indexing metadata

Copyright (c) 2025 Kuznetsov V.А., Kostryukov A.A.