Мақаланы E-mail арқылы жіберу Radiation resistance of thermo stabilizing barium titanate coatings for space aircrafts
- Авторлар: Mikhailov MM1, Lapin AN1
-
Мекемелер:
- Шығарылым: Том 11, № 1 (2010)
- Беттер: 134-136
- Бөлім: Articles
- URL: https://journals.eco-vector.com/2712-8970/article/view/508640
- ID: 508640
Дәйексөз келтіру
Толық мәтін
Аннотация
Comparative analysis of diffuse reflectance spectra, integral absorption factors and their change after electron irradiation (Е = 30 keV) for barium titanate coatings doped with aluminum oxide and zirconium oxide (Ba0,6Al0,4TiO3 and BaTi0,7Zr0,3O3) was carried out. It was found out that the use of Al2O3 and ZrO2 nano Powders instead of micro powders for doping BaTiO3 increases radiation resistance of the coatings.
Негізгі сөздер
Әдебиет тізімі
- Михайлов М. М., Соколовский А. Н. Пигменты для термостабилизирующих покрытий // Известия вузов. Физика. 2007. № 12. С. 90-91.
- Elektronical propertiecs of (Ba,Sr)TiO3 on (Sr,Ca)RuO3 elektrode / Seung Yong San [at al.] // J. Mater. Sci. 1999. Vol. 34. P. 6115-6119.
- Ларин B. К., Кондаков B. М., Дедов Н. B. Плазмохимический способ получения ультрадисперсных (нано) порошков оксидов металлов и перспективы их применения // Известия вузов. Цветная металлургия. 2003. № 5. С. 59-64.
- Установка для исследования спектров диффузного отражения и люминесценции твердых тел в вакууме / Л. Г. Косицин [и др.] // ПТЭ. 1985. № 4. С. 176-180.
- Johnson F. S. The solar constant // J. Metrological. 1954. Vol. 11. № 6. P. 431-439.
Қосымша файлдар